4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯 TDE-85

             可采用脂肪族和芳香族胺类、酸酐及咪唑类作为固化剂。固化产物热稳定性好，以间苯二胺固化的马丁耐热温度为185°C，而以酸酐固化的马丁耐热温度为156°C ，加工工艺性能好，其固化物具有耐高温、高强度、高连接性等特点，耐候性、耐低温性和电绝缘性也很好，

             可用于航空、航天、核动力、电子等多个领域。本环氧树脂的碳纤维、玻璃纤维复合材料已经制成了高性能飞机用的结构材料。在核动力工业中,应用在具有特殊力学性能的部件上。该树脂可制成高强度、高弹性模量的碳纤维体育器材, 也可制造耐高温高压的大型户外工频设备，还可作耐高温胶黏剂、无溶剂漆、耐高温绝缘铸料和包封材料等。用于配制耐高温环氧树脂胶黏剂, 在150℃下黏结强度比E型环氧树脂体高6~8倍，T型剥离强度提高50%。

●技术指标：

 包装贮存： 1kg和5kg  20kg桶装，长期保存至温度为2-40℃的条件下。

4,5-epoxytetrahydrophthalic acid diglycidylester

7-Oxabicyclo[4.1.0]heptane-3,4-dicarboxylate de bis(2-oxiranylméthyle) [French] [ACD/IUPAC Name]
7-Oxabicyclo[4.1.0]heptane-3,4-dicarboxylic acid, bis(oxiranylmethyl) ester [ACD/Index Name]
Bis(2-oxiranylmethyl) 7-oxabicyclo[4.1.0]heptane-3,4-dicarboxylate [ACD/IUPAC Name]
Bis(2-oxiranylmethyl)-7-oxabicyclo[4.1.0]heptan-3,4-dicarboxylat [German] [ACD/IUPAC Name]
Bis(oxiran-2-ylmethyl) 7-oxabicyclo[4.1.0]heptane-3,4-dicarboxylate
25293-64-5 [RN]
3,4-BIS(OXIRAN-2-YLMETHYL) 7-OXABICYCLO[4.1.0]HEPTANE-3,4-DICARBOXYLATE
4,5-Epoxycyclohexane-1,2-dicarboxylic acid diglycidyl ester
4,5-epoxytetrahydrophthalic acid diglycidylester
Bis(oxiran-2-ylmethyl)7-oxabicyclo[4.1.0]heptane-3,4-dicarboxylate
BIS(OXIRAN-2-YLMETHYL)-7-OXABICYCLO-[4.1.0]-HEPTANE-3,4-DICARBOXYLATE
Bis[(oxiran-2-yl)methyl] 7-oxabicyclo[4.1.0]heptane-3,4-dicarboxylate
Diglycidyl 4,5-epoxycyclohexane-1,2-dicarboxylate
Diglycidyl 4,5-epoxycyclohexane-1,2-dicarboxylate (S-186)
MFCD13194833 [MDL number]

This product is a trifunctional epoxy resin containing an alicyclic epoxy group and a glycidyl ester group in the molecular structure, and has the dual characteristics of an alicyclic epoxy and a glycidyl ester, and is also called a mixed epoxy resin. Due to the existence of a highly reactive glycidyl ester group, the reactivity is greater than that of general alicyclic epoxy resins, the epoxy value is higher, the viscosity is lower, and the solubility with the curing agent is good, and aliphatic and aromatic can be used Amines, anhydrides and imidazoles are used as curing agents. The cured product has good thermal stability. The heat-resistant temperature of Martin cured with m-phenylenediamine is 185 ° C, and the heat-resistant temperature of Martin cured with acid anhydride is 156 ° C. The processing performance is good, and the cured product has high temperature and high resistance. Features such as strength, high connectivity, weather resistance, low temperature resistance and electrical insulation are also very good, and can be used in many fields such as aviation, aerospace, nuclear power, electronics and so on. The carbon fiber and glass fiber composite materials of the epoxy resin have been made into structural materials for high performance aircraft. In the nuclear power industry, it is applied to components with special mechanical properties. The resin can be made into carbon fiber sports equipment with high strength and high modulus of elasticity, and it can also be used to manufacture large-scale outdoor power frequency equipment that is resistant to high temperature and high pressure. Sealing material, etc. It is used to formulate high temperature resistant epoxy adhesives. At 150 ° C, the bonding strength is 6 to 8 times higher than that of E-type epoxy resin bodies, and the T-type peel strength is increased by 50%.

4,5-エポキシヘキサヒドロフタル酸ジグリシジル

本製品は、分子構造中に脂環式エポキシ基とグリシジルエステル基を含む三官能性エポキシ樹脂であり、脂環式エポキシとグリシジルエステルの二重の特徴を持ち、混合エポキシ樹脂とも呼ばれます。高度に反応性のグリシジルエステル基の存在により、反応性は一般的な脂環式エポキシ樹脂よりも大きく、エポキシ価は高く、粘度は低く、硬化剤との溶解性は良好であり、脂肪族および芳香族の缶はアミン、無水物、およびイミダゾールが硬化剤として使用されます。硬化物の熱安定性は良好です。 m-フェニレンジアミンで硬化したマーチンの耐熱温度は185°Cであり、酸無水物で硬化したマーチンの耐熱温度は156°Cです。加工性能は良好であり、硬化物は高温および高抵抗です。強度、高い接続性、耐候性、低温耐性、電気絶縁などの機能も非常に優れており、航空、航空宇宙、原子力、電子機器などの多くの分野で使用できます。エポキシ樹脂の炭素繊維とガラス繊維の複合材料は、高性能航空機の構造材料になりました。原子力産業では、特殊な機械的特性を持つコンポーネントに適用されます。この樹脂は、高強度と高弾性率を備えた炭素繊維スポーツ用品にでき、また、高温高圧に耐える大規模な屋外電力周波数機器の製造にも使用できます。シーリング材など。耐高温エポキシ接着剤の配合に使用されます。 150°Cでは、接着強度はEタイプのエポキシ樹脂本体の6〜8倍高く、Tタイプの剥離強度は50％増加します。

4,5- 에폭시 테트라 히드로 프탈산 디 글리시 딜 에스테르

이 생성물은 분자 구조에 지환 식 에폭시기 및 글리시 딜 에스테르기를 함유하는 3 관능 에폭시 수지이며, 지환 식 에폭시 및 글리시 딜 에스테르의 이중 특성을 가지며, 혼합 에폭시 수지라고도한다. 반응성이 높은 글리시 딜 에스테르 기의 존재로 인해 반응성이 일반적인 지환 족 에폭시 수지보다 높으며, 에폭시 값이 높고, 점도가 낮으며, 경화제에 대한 용해성이 양호하며, 지방족 및 방향족 캔 아민, 무수물 및 이미 다졸이 경화제로서 사용된다. 경화물은 우수한 열 안정성을 갖는다. m- 페닐 렌 디아민으로 경화 된 마틴의 내열 온도는 185 ° C이고, 산 무수물로 경화 된 마틴의 내열 온도는 156 ° C이다. 가공 성능은 양호하고, 경화물은 고온 및 고 저항을 갖는다 . 강도, 높은 연결성, 내후성, 저온 저항 및 전기 절연과 같은 기능도 매우 우수하며 항공, 항공 우주, 원자력, 전자 제품 등과 같은 많은 분야에서 사용할 수 있습니다. 에폭시 수지의 탄소 섬유 및 유리 섬유 복합 재료는 고성능 항공기를위한 구조 재료로 만들어졌다. 원자력 산업에서는 특수한 기계적 성질을 가진 구성 요소에 적용됩니다. 수지는 높은 강도와 ​​높은 탄성 계수를 갖는 탄소 섬유 스포츠 장비로 제조 될 수 있으며, 고온 및 고압에 강한 대규모 실외 전력 주파수 장비를 제조하는데 사용될 수있다. 밀봉재 등 고온 내성 에폭시 접착제를 제조하는 데 사용됩니다. 150 ℃에서, 결합 강도는 E- 타입 에폭시 수지 바디의 결합 강도보다 6 내지 8 배 높고, T- 타입 박리 강도는 50 % 증가된다.